Structure evolution of [ BDTA(PEO)_x] _n alternate copolymers when mixed with a lithium salt

¹ Université J. Fourier Grenoble I, Laboratoire de Spectrométrie Physique, UMR 5588 du CNRS, BP. 87, 38402 Saint-Martin-d'Hères cedex, France
² CEA-CEN Grenoble, DRFMC, SI3M, 17 rue des Martyrs, 38054 Grenoble cedex 9, France
³ Centre Universitaire Paris Sud, Laboratoire d'Utilisation du Rayonnement Électromagnétique, 91405 Orsay cedex, France
⁴ ENSEE Grenoble, Laboratoire d'Électrochimie et de Physique des Matériaux et des Interfaces, Domaine Universitaire, BP. 75, 38402 Saint-Martin-d'Hères cedex, France
⁵ Université de Montréal, Département de Chimie, Québec, Canada

Abstract

The structure of three jeffamine-pyromellitimides based alternate copolymers were studied by small angle X-ray scattering measurements when they are mixed with a lithium salt. The salt addition contributes to increase the elastic domain of compounds with the longest units (B900 and B2000). By contrast, the salt induces the system having the shortest repeat units (B600) to stiffen and to crystallize.

Résumé

La structure de trois copolymères alternés à base de jeffamine et d'unités pyromellitimides mélangés avec un sel de lithium a été étudiée par diffusion des RX aux petits angles. La présence du sel contribue à augmenter le domaine caoutchoutique des composés aux unités les plus longues (B900 et B2000). Par contre, le système le plus court (B600) se rigidifie et cristallise.