Oxidation of titanium in steam atmosphere within the temperature range of 300-1200°C

Quantitative Analysis Department, Faculty of Chemistry, Leningrad State University, 7/9, Universitetskaya Naberejnaya, Leningrad, 199034, USSR, U.S.A..

Abstract

Titanium oxidation kinetics were studied by a gravimetric method in flowing steam medium at 300-1200°C. Kinetic laws of general oxidation process, scale growth, diffusion oxygen layer formation and hydrogen absorption on metal phase are established. Besides, temperature dependence of rate constants and absorbed hydrogen content in metal, as well as scale phase analysis are determined. Certain aspects of scale formation mechanism and hydrogen influence upon titanium oxidation were studied.

Résumé

A l'aide de la méthode gravimétrique la cinétique de l'oxydation du titane a été mise à l'étude dans un courant de la vapeur d'eau à 300-1200°C. Ainsi ont été établies les lois cinétiques du processus général d'oxydation, de la croissance de la couche d'oxyde, de la formation de la couche diffusionnelle d'oxygène et de l'absorption de l'hydrogène par la phase métallique. En outre a été également déterminée la dépendance de température des constantes de vitesse et de la teneur du métal en hydrogène absorbé ainsi que la composition immédiate de la couche d'oxyde. La lumière a été faite sur certains aspects du mécanisme de sa formation et de l'influence de l'hydrogène sur l'oxydation du titane.