Excess enthalpies of liquid Bi-Ge-Te alloys

Institut für Chemie, Universität Osnabrück, Barbarastr 7, D-49069 Osnabrück, Germany.

Abstract

The excess enthalpies of liquid alloys in the ternary system Bi-Ge-Te were determined at 1193 K in a heat flow calorimeter for five sections Bi_yGe_1-y-Te with y = 0.2. 0.4, 0.5, 0.6 and 0.8. The enthalpy surface in the ternary system is characterized by a valley stretching from the exothermic minimum in the system Ge-Te to the exothermic mimimum in the system Bi-Te. The analytical description of the excess enthalpies in the limiting binaries was made with the Redlich-Kister formalism. For the description of the thermodynamic functions in the ternary system the equation of Bonnier was taken using additional ternary coefficients. The calculated curves obtained from the optimization are in good agreement with the experimental data.

Résumé

Les descriptions de F enthalpies d'excès dans les alliages liquides du système ternaire Bi-Ge-Te ont été mesurées à 1193 K par calorimétrie haute temperature pour les cinq sections Bi_yGe_1-y-Te avec y = 0.2, 0.4, 0.5, 0.6 et 0.8. La surface enthalpique du système ternaire est représentée par une vallée qui s'étend du de la minimum exothermique du système Ge-Te au minimum exothermique du système Bi-Te. La description analytique de Tenthalpie d’excès des systèmes binaires limitrophes a été réalisée suivant le formalisme de Redlich-Kister. Les fonctions thermodynamique ont été modélisées suivant la relation de Bonnier en utilisant des coefficients ternaires additionels. Les courbes calculés à partir des fonctions optimisées sont en bon accord avec l’experience.