Effect of incident light flux and hydrogen peroxide on the characteristics of single crystals of αFe₂O₃ anodes

¹ Laboratoire d’Electrochimie Interfaciale du CNRS, 92195 Meudon, France.
² Permanent adress : Chemistry Department, Faculty of Science, Ain Shams University, Abbassia, Cairo, Egypt.

Abstract

Electrochemical characterization of n-αFe₂O₃/aqueous electrolyte junctions was carried out In darkness and under illumination. Effect of some redox species on the current-voltage response of the studied anodes was realized. The role of the Incident light flux on the n-αFe₂O₃/electrolyte junction has been determined. Cathodic shifts of the steady-state photocurrent onset potential of αFe₂O₃ anodes have been achieved upon decreasing the Illuminating light flux. At the highest light intensity used, the same cathodic shift was noticed when H₂O₂ was added to the electrolyte Platband potential values were determined using two different techniques. Intraband transitions are given in terms of direct (2.67 eV) and indirect (1.98 eV) bandgaps.

Résumé

Le comportement électrochimique d’électrodes en αFe₂O₃ de type n a été étudié en milieu aqueux à l’obscurité et sous éclairement en l’absence et en présence de couples rédox. Le rôle du flux lumineux Incident sur la réponse de la jonction a été déterminé : des déplacements du potential de démarrage du photocourant stationnaire vers les potentiels négatifs ont été observés en faisant décroître l’intensité du flux lumineux. Pour le flux lumineux le plus Intense utilisé, le même déplacement négatif a été observé quand H₂O₂ était ajouté au milieu. Les valeurs des potentiels de bandes plates ont été mesurées par deux techniques différentes : les transitions interbandes ont pu être déterminées 2,67 eV pour la transition directre et 1,98 eV pour la transition Indirecte.