Standard enthalpies of formation of yttrium alloys, Y-Me (Me = Ru, Rh, Pd, Os, Ir, Pt), by high-temperature calorimetry

James Franck Institute, University of Chicago, 5640 S Ellis Avenue, Chicago, IL 60637, USA.

Abstract

The standard enthalpies of formation of yttrium alloys, Y Me (Me = Ru, Rh, Pd, Os, Ir, Pt) were determined by direct synthesis calorimetry at 1473 ± 2 K. The following values of [math] are reported (J/mole of atoms) : Ru₂Y5, - (27.3 ± 3.1), RhY, - (76.1 ± 3.4) ; Rh₂Y, - (65.4 ± 1.3) ; PdY, - (94.9 ± 3.8) ; Pd₄Y3, - (92.8 ± 3.7) ; Pd₃Y, - (79.0 ± 6.5) ; Os₂Y, - (24.8 ± 2.8) ;IrY, - (65.9 ± 3.8) ; Ir₂Y, - (59.4 ± 2.8) ; PtY, - (104 ± 2.3) ; Pt₃Y, - (86.9 ± 2.0). The results are compared with the predictions of the models, and with earlier data for some of the corresponding zirconium alloys.

Résumé

Les enthalpies standard de formation des alliages d’yttrium Y Me (Me = Ru, Rh, Pd, Os, Ir, Pt) ont été déterminées par calorimétrie de synthèse directe à 1473 ± 2 K. Les résultats suivants ont été obtenus pour [math] en joules par moles d'atomes : Ru₂Y5, -(27.3 ± 3.1), RhY, -(76.1 ± 3.4) ; Rh₂Y, -(65.4 ± 1.3) ; PdY, -(94.9 ± 3.8) ; Pd₄Y3, -(92.8 ± 3.7) ; Pd₃Y, -(79.0 ± 6.5) ; Os₂Y, -(24.8 ± 2.8) ; IrY, -(65.9 ± 3.8) ; Ir₂Y, -(59.4 ± 2.8) ; PtY, -(104 ± 2.3) ; Pt₃Y, - (86.9 ± 2.0). Les résultats sont comparés avec les prévisions des modèles et avec des valeurs déjà obtenues pour les alliages correspondants à base de zirconium.