Standard enthalpies of formation of some refractory borides of 4d and 5d elements from high-temperature direct synthesis calorimetry

James Franck Institute, The University of Chicago, 5640 S Ellis Avenue, Chicago, IL 60615, USA.

Abstract

The standard enthalpies of formation of YB₂, TaB₂, and W₂B₅ have been determined by direct synthesis calorimetry at 1473 ± 2 K. The following values are reported: [math] (YB₂) = -35.7 ± 2.6 kJ/g.atom; [math] (TaB²) = -53.3 ± 2.0 kj/g.atom; [math](W₂B₅) = -17.5 ± 1.1 kJ/g.atom. Two new techniques which facilitate completeness of reactions at the calorimeter temperature are discussed. The results are compared with available thermodynamic data from the Literature and with predicted values from Miedema's semi-empirical model.

Résumé

Les enthalpies standard de formation de YB₂, TaB₂ et W2B₅ ont été déterminées par calorimétrie de synthèse directe à 1473 ± 2 K. Les résultats suivants sont obtenus : [math] (YB₂) = - 35.7 ± 2.6 kJ/mole d’atomes, [math](TaB₂) = - 53.3 ± 2 kJ/mole d’atomes, [math](W₂B₅) = - 17.5 + 1.1 kJ/mole d'atomes. Deux nouvelles techniques qui facilitent l’obtention de réactions complètes à la température du calorimètre sont discutées. Les valeurs obtenues sont comparées avec des données de la littérature et avec les prévisions du modèle semi-empirique de Miedema.