TCE adsorption on hydrophobic Y and MFI zeolites. Possibilities of using such materials for solvent recovery

Laboratoire de recherches sur la réactivité des solides, université de Bourgogne, France.

Abstract

The isotherms of the adsorption of water and tetrachloroethene (TCE) on dealuminated Y and ZSM-5 zeolites have been drawn at 25°C to characterize the hydrophobic/organophilic properties and the porosity of the adsorbents. The amounts of solvent adsorbed in pure vapor phase or in the room atmosphere differ only slightly because of the hydrophobic character of the adsorbents. Such hydrophobic dealuminated zeolites show a high capacity for TCE adsorption. Contrary to activated carbon, a TCE saturated dealuminated Y faujasite can be completely regenerated at low temperature (T < 100°C). Thereby it would be interesting to be used for solvent recovery.

Résumé

Des isothermes d'adsorption de la vapeur d'eau et du tétrachloroéthène (TCE) ont été tracées à 25°C pour étudier le caractère hydrophobe et organophile et la porosité de faujasites Y et d'une zéolithe ZSM-5 désaluminées. Les quantités de solvant adsorbé en phase vapeur pure ou en atmosphère ambiante sont peu différentes du fait du caractère hydrophobe des échantillons. Ces derniers présentent une grande capacité d'adsorption vis-à-vis du TCE. Contrairement au charbon actif, une zéolithe Y désaluminée saturée avec du TCE peut être totalement regénérée à basse température (T < 100°C) et de ce fait son utilisation potentielle pour une récupération propre des solvants est digne d'intérêt.