Surface properties of polycarbonate and promotion of yeast cells adhesion
Unité de Chimie des Interfaces, Université Catholique de Louvain, Place Croix du Sud, 1, B-1348 Louvain-la-Neuve, Belgium.
Bonding of sulfate groups is the main surface modification occuring when polycarbonate plates are oxidized by K2Cr2C7-H2SO4. Contact of un- or oxidized polycarbonate with a supersaturated ferric solution gives rise to deposition of ferric hydroxide which produces a charge reversal and allows adhesion of a dense layer of yeast cells. Successive application of the two treatments avoids a loss of the cell adhesion promoting efficiency when the support is dried after the Fe treatment; this is attributed to better anchoring of ferric hydroxide on the strongly negative surface obtained after oxidation.
Résumé
L’oxydation de plaques de polycarbonate par le mélange K2Cr2C7-H2SO4 provoque surtout la fixation de groupements sulfate sur la surface. Un contact du polycarbonate, comme tel ou oxydé, avec une solution ferrique sursaturée donne lieu au dépôt de particules d’hydroxyde ferrique, qui sont responsables d’une inversion de la charge électrique et permettent l’adhésion d’une couche dense de cellules de levure. L’application préalable du traitement oxydant permet de conserver la capacité de fixer les cellules lorsque le matériau est séché après application du traitement au fer ; ceci est attribué à un meilleur ancrage des particules d’hydroxyde ferrique sur la surface fortement négative.
© Paris : Société de Chimie Physique, 1987