Metastable intermetallics in the Zn-Mn system obtained by electrodeposition
1 Dipartimento di Chimica Fisica Applicata, Politecnico di Milano V Mancinelli 7, 1-20131, Milan.
2 Soc Pneumatici Pirelli, Business Unit Steelcord V Petrarca 104, 1-50063 Figine Valdarno, Italy
.
Metastable phases of the Zn-Mn system can be prepared at low temperature by electrochemical methods. ε and ε βBCC alloys can be obtained as a function of the operating conditions. Structural studies are reported concerning the thermal stability of the metastable phases, their grain growth behaviour and their stress state as a function of heat-treatment time and temperature. Equilibrium structures cannot be obtained by heating the ε phase below the eutectoidic temperature, equilibrium α’ can be precipitated from metastable βBCC.
Résumé
Les phases métastables du systèmes Zn-Mn peuvent être préparées à basse température par le biais de méthodes électrochimiques. Des alliages ε et ε βBCC peuvent être obtenus en fonction des conditions opératives. Des études structurelles ont été rapportées concernant la stabilité thermale des phases métastables, leur comportement de croissance des grains et leur état de tension en fonction du temps de traitement à la chaleur et de la température. Les structures d’équilibre ne peuvent être obtenues en réchauffant la phase ε en-dessous de la température eutectoidique ; la phase d’équilibre α’ peut être précipitée par la phase métastable βBCC.
Key words: Electrodeposition / metastable phases / X-ray diffraction / grain growth
Mots clés : Electrodéposition / phases métastables / diffraction de rayons X / croissance des grains