Molar heat capacity of some Au+Pb alloys

¹ Département de génie chimique, centre de recherches de Royallieu, université de Compiègne, 60206 Compiègne cedex, France.
² IUSTI, UMR 139, université de Provence, avenue Escadrille Normandie-Niemen, 13397 Marseille cedex 20 Contribution to the conference on “Thermodynamics of alloys 96", Marseille, September 2-5, 1996, France.

Abstract

The molar heat capacities of some Au-Pb alloys were determined at constant pressure in the temperature range 423 K-773 K by using differential scanning calorimetry ; the studied alloys are the three intermetallic compounds Au₂Pb, AuPb₂ and AuPb₃, the eutectic alloy and the Au_0.5Pb_0.5, Au_0.4Pb_0.6 et Au_0.3Pb_0.7 alloys. These values have been smoothed and expressed as function of T-T₀.

From Cp° results obtained in solid and liquid state, the excess molar heat capacities were deduced.

Résumé

Cette étude thermodynamique est relative à la détermination, par calorimétrie à balayage, des capacités calorifiques molaires des composés intermédiaires Au₂Pb. AuPb₂ and AuPb₃, des alliages de composition xPb = 0.50, 0.60, 0.70 et de l'alliage eutectique XPb = 0.841.Les résultats obtenus à l'état solide et à l'état liquide, pour chaque alliage étudié, ont été exprimés sous une forme linéaire.

L'exploitation de ces données experimentales a permis d'évaluer les capacités calorifiques d'excès (ΔCp° = Cp°(exp) - Cp°(add)) aux températures de 453 K, 503 K, 573 K and 773 K.