Study of phase equilibria in the Al-Cu-Zr system at the Al-rich part

University of Minho, Institute of Materials, Azurèm, 4800 Guimaräes, Portugal.

Abstract

The Al-rich side of the Al-Cu-Zr system was studied employing microstructural and DTA analysis. The alloys contained up to 14 at.% Zr and 25 at.% Cu. The phases detected were in agreement with the literature for this system, except for the appearance of a “new” phase replacing the phase τ9 cited in the literature, and which has never been identified in this study.

The temperatures of the phase transformations were determined by DTA. The equilibrium phases present in the alloys have been identified on samples annealed at temperatures higher and lower than the temperatures of transformation. A reaction scheme is proposed for the transformations occurring at this part of the system.

Résumé

La partie riche en aluminium du système Al-Cu-Zr a été étudiée par analyse thermique différentielle et par microscopie. Les alliages contenant jusqu'à 14 at.% Zr et 25 at.% Cu ont présenté des phases en bon accord avec celles mentionnées dans la littérature, à l'exception d'une “nouvelle” phase qui a été mise en évidence à la place de la phase τ9 citée dans la littérature mais jamais trouvée durant cette étude. Les températures des transformations de phases ont été déterminées par ATD.

Les phases en équilibre dans les alliages ont été identifiées sur des échantillons qui ont subi des traitements d'homogénéisation à des températures supérieures et inférieures aux températures de transformation. Les auteurs proposent un schéma réactionnel plausible pour cette partie du système ternaire.