Investigation of ageing effects in PANI-CSA by conductivity and structural measurements

¹ Laboratoire de Physique des Métaux Synthétiques, UMR 5819, CEA-CNRS-UJF, Département de Recherche Fondamentale sur la Matière Condensée, CEA-Grenoble, 38054 Grenoble cedex 9, France
² Laboratoire de Spectrométrie Physique, UMR 5588 du CNRS, Université Joseph Fourier Grenoble I, BP. 87, 38402 Saint-Martin-d'Hères cedex, France

Abstract

Thermal ageing effect on the highly conducting CSA-PANI was investigated by measurements of the thermal dependence of the conductivity and by X-ray studies of the structure. The non-aged sample shows a metallic-like conductivity around room temperature (RT) and activated behavior dominates the low temperatures. With ageing, the metallic character at RT vanishes, whereas 16% of the sample is still crystalline after 20 days of ageing. A preliminary analysis of the data is carried out using a simple combination of a metallic and a hopping term in series.

Résumé

Les effets du vieillissement thermique sur les films PANI-CSA ont été étudiés sur la conductivité et la structure cristallographique. Avec le vieillissement, le maximum de conductivité se déplace vers les hautes températures et le comportement quasi-métallique disparaît. Cependant une fraction cristalline de 16 % subsiste dans les échantillons très longuement vieillis. Une analyse préliminaire des résultats est effectuée avec un modèle simple dans lequel la résistivité se compose d'un terme métallique et d'un terme de hopping en série.