Ul₄ compound : determination of high temperature phase transitions from electrical conductivity and calorimetric measurements

¹ Laboratoire de Dynamique et Thermophysique des Fluides, associé au C.N.R.S. Université de Provence, Centre de St. Jérôme, 13397 Marseille Cedex 13, France.
² Institut de Chimie Inorganique et de Métallurgie des Eléments Rares, Ecole Polytechnique de Wroclaw. Wybrzeze Wysplansklego 27, 50-370 Wroclaw, Pologne.

Abstract

Two complementary techniques — electrical conductivity and calorimetric measurements — were used to evidence the high temperature phase transitions in the Ul₄ compound. The existence of a “premelting effect” was clearly detected from these both series of observations, identical to that previously found for the similar compound UBr₄, two more transformations appearing in solid Ul₄.

The temperatures and the enthalpies associated with these solid-solid and solid-liquid transformations were determined.

Résumé

Deux techniques complémentaires permettant la mesure de la conductivité électrique et des accroissements enthalpiques ont mis en évidence l’existence, à haute température, de transitions de phase pour le composé UI₄.

L’existence d’un “effet de préfusion” a été clairement détectée à partir de ces deux séries d’observations, effet identique à celui déjà trouvé pour le composé similaire UBr₄, par ailleurs deux transformations supplémentaires apparaissent dans UI₄ solide.

Les températures et les variations d’enthalpie associées à ces transformations solide-solide et solide-liquide ont été déterminées.