Preparation, stoichiometry and structure of fluorine intercalated graphite fibers
1
Department of Industrial Chemistry and Division of Molecular Engineering, Kyoto University, Kyoto 606, Japan.
2
Faculty of Engineering, Shinshu University, Nagano 380, Japan.
Fluorine intercalated graphite fibers have been prepared from direct reactions of the heat-treated benzene derived vapor grown carbon fiber with elemental fluorine at temperatures between 330-614 °C. An attractive feature of the fiber as a pristine graphite is that it can readily be intercalated by fluorine with lower threshold of formation temperature and time. The compounds obtained at around 600 °C are of stage-1 and those obtained at lower temperature range between 330-380 °C are of stage-2. Mixed stage compounds are formed in the intermediate temperatures.
The relation between stoichiometry and stage of these comoounds have been clarified in connection with crystal structure.
Résumé
Des fibres de fluorure de graphite ont été synthétisées par fluoruration directe de fibres de carbone, obtenues par décomposition thermique de dérivés benzèniques. La fluoruration a été assurée à partir de fluor gazeux à des températures comprises entre 330 et 614 °C. Un point intéressant de ces fibres de carbone est qu'il est possible d'y intercaler facilement le fluor, dans des conditions de température et de temps minimales. Les composés obtenus à environ 600 °C sont du premier stade, tandis que ceux obtenus à une température plus basse, entre 330 et 380 °C, sont du deuxième stade. Un mélange de ces composés est observé à des températures intermédiaires.
Une relation entre stoechiométrie et stades d'intercalation a été mise en évidence, en liaison avec les structures cristallines.