Chemico-physical characterization of the poly(tetrahalo-P-phenyleneselenide)s semiconducting polymers

¹ Laboratoire de Polimeros, Facultad de Quimica, Universidad Catollca de Chile, PO Box 6177, Santiago Chili, Chili.
² laboratoire de physique des matériaux pour l'électronique, faculté des sciences et des techniques, université de Nantes, 2, rue de la Houssinière, 44072 Nantes Cedex, France.

Abstract

Chemico-physical characterization of semiconducting polymers having selenium in the chain have been done by XPS, microprobe analysis and optical absorption. The binding energy of Se3d peak shows that there are positive partial charges on the selenium atoms. The high chemical shift of the Cls binding energy in the case of C-Br is attributed to the s-character of bromine when bound to carbon. This s-character gives an effective electronegativity higher than Pauling’s value. After doping, the binding energy of the dopant (Cl or I) corresponds to the anion position. Therefore we can imagine that during doping there is polaron or bipolaron formation. The hypothesis of polaron formation is conforted by optical absorption experimental results. The homogeneity of the powder has been checked by microprobe analysis. The relative concentrations are nearly the one expected.

Résumé

Une étude par XPS a été réalisée sur des polymères semiconducteurs de la famille des polytrétrahol-p-phenyleneselenides. Les résultats montrent que les atomes de Se sont partiellement chargés positivement. De même la valeur élevée de l'énergie de liaison du Br est attribuée au caractère s du Br lié au C. Après dopage les halogènes dopant (Cl ou I) sont à l'état d'anions.