Short and long range orders in FeV alloys experiments and cluster variation calculations
1
IPCMS-GEMME, 4, rue Blaise-Pascal, F-67070 Strasbourg, Strasbourg.
2
ONERA, 29, avenue de la Division-Leclerc, F-92320 Châtillon-sous-Bagneux, France.
3
MPI für Eisenforschung GmbH, Max-Planck Strasse 1, D-4000 Düsseldorf, Germany.
4
Laboratoires Léon-Brillouin, CEN Saclay, F-91190 Gif-sur-Yvette, France.
The FeV phase diagram is revisited. Using neutron scattering in a single crystalline FeV20at%, the B2 long range order parameter has been measured. The homogeneous disordered range is found to start at 990 K. TEM observations on a FeV30at% sample give some indications that according to the heat treatement a single phase B2 or a two phase A2 + B2 zone can be observed at low temperature. The results are in agreement with a paramagnetic CVM calculation using a previous SRO determination of the pair interaction potentials.
Résumé
Nous revisitons le diagramme de phase FeV. Le paramètre d'ordre associé à la phase B2 est suivi par diffraction de neutrons sur un monocristal FeV20at%. Le domaine désordonné homogène commence à 990 K. Des observations par TEM sur un échantillon Fe30at% suggèrent que selon le traitement thermique, on observe à basse température un domaine monophasé B2 ou bi-phasé B2+A2. Ces résultats concordent avec ceux obtenus par CVM dans le domaine paramagnétique à partir des énergies d’interaction de paires déduites de la mesure d’ordre local.