Thermodynamic investigation on glass forming AI-RE Systems

¹ Dipartimento di Chimica Inorganica, Chimica Fisica e Chimica dei Materiali, Università di Torino, Via P Giuria 9, 10125 Torino, Italy.
² Istituto di Chimica Generale, Università di Genova, Viale Benedetto XV 3, 16132 Genova, Viale Benedetto XV 3, 16132 Genova, Italy.

Abstract

Data for the specific heat of solid and liquid phases, heat and temperature of melting are given for Al₉₁Ce₉, Al₉₄Ce₆, Ce₇₀Al₃₀, Ce₇₅Al₂₅, Al₉₁,Nd₉, and Al₈₆Nd₉Fe₅ alloys as determined by DSC. Rapid solidification of the alloys resulted in either fully or partially amorphous samples. Values for the heat and temperature of crystallization are also reported. The role of an excess liquid specific heat with respect to crystal phases in glass formation is outlined.

Résumé

Les chaleurs spécifiques des phases solides et liquides, la chaleur et la température de fusion des alliages Al₉₁Ce₉, Al₉₄Ce₆, Ce₇₀Al₃₀, Ce₇₅Al₂₅, Al₉₁Nd₉ et Al₈₆Nd₉Fe₅ ont été mésurées par DSC. La solidification rapide des alliages produit des échantillons totalment ou partiellement amorphes. Les valeurs de la chaleur et de la température de crystallisation ont aussi été mesurées. Pour ce qui concerne la formation d’un phase vitreuse, le rôle de l'éxcès de la chaleur spécifique du liquide par rapport a celui des phases crystallines a été mis en évidence.