Partial enthalpies of solution in liquid binary alloys from photoelectron spectroscopy

¹ Freie Universität Berlin, Institut für Experimentalphysik, D-1000 Berlin 33, France.
² Universität Basel, Institut für Physik CH-4056 Basel, Switzerland.

Abstract

In photoemission experiments (XPS, UPS) we have determined the binding energy shifts of AI2p, and Ge3d levels in liquid Al_xGe_y alloys as a function of alloy composition (0.40 ≤ x ≤ 0.88). From these data ternary partial enthalpies of solution at infinite dilution of Si, As in AlxGey have been derived in a Bom- Haber cycle framework. Good agreement of the results with binary partial enthalpies of solution from Miedema's semiempirical scheme was found for the dilute limits of alloy composition x → 0 and x → 1. Comparison with the cases of Au-Ga and Au-Sn is made.

Résumé

Nous avons déterminé par spectroscopie d'électrons (XPS, UPS) les déplacements des niveaux d'énergie AI2p et Ge3d dans l'alliage liquide Al^xGe^y en fonction de la composition (0.40 ≤ x ≤ 0.88). A partir des résultats, les enthalpies partielles à dilution infinie de Si et As dans AlxGey ont été dérivées en s'appuyant sur le cycle de Born-Haber. L'agrément entre nos valeurs et celles du modèle semiempirique de Miedema est bon pour les dilutions limites x → 0 et x → 1. Des comparaisons avec les cas de Au-Ga et Au-Sn sont faites.