Investigations in the ternary systems V-Si-C and Ta-Si-C
Institut tür Physikalische Chemie, Universität Wien, Währingerstrasse 42, A-1090 Wien, Austria.
Within a series of papers dealing with phase diagrams relevant to joining ceramics to metals the binary systems V-Si-C and Ta-Si-C are investigated.At 1000°C only one ternary phase,M5Si3C1-x(M=V,Ta) is observed in each system.VsSi3C1-x coexists with SiC,VC,VsSi3 and VSi2 thus dominating the isothermal section.In contrast,TasSi3C0.5 coexists with TaC, Ta2C, Ta2Si, TasSi3 and TaSi2 but not SiC, because TaC is the dominating phase in this system.Nevertheless,the thermochemical stabilities of the two ternary phases,as derived from the observed phase equilibria and thermochemical data of the binary boundary phases,turn out to be identical within the uncertainty limits of the method.
Résumé
Dans une série de publications traitant des liaisons céramiques - métaux et des diagrammes ternaires appropries, les systèmes V-Si-C et Ta-Si-C sont étudies. A 1000°C, un seul compose ternaire M5Si3C1-x (M = V, Ta) apparait dans ces systèmes. V5Si3C1-x est en équilibre thermodynamique avec SiC, VC, V5Si3 et VSi2 et se présente donc comme la phase dominante dans cette section isotherme. Ta5Si3C0,5 au contraire est en équilibre avec TaC, Ta2C, Ta2Si, Ta5Si3 et TaSi2 mais n'est pas en équilibre avec Sic, car la phase dominante dans ce system est TaC. Néanmoins les stabilités thermochimiques déduites des équilibres des phases observées et des données thermodynamiques des phases binaires sont identiques dans la gamme d'incertitude de la méthode.
© Elsevier, Paris, 1993