Modelling non-stoichiometric phases in the system Al-Cu-Mg-Zn
1 Lehrstuhl für theoretische Hüttenkunde, RWTH, Kopernikusstr 16, D-52054, Aachen.
2 Max-Planck-Institut für Metallforschung, PML, Heisenbergstr 5, D-70569 Stuttgart, Germany.
Thermodynamic databases for multicomponent systems are proving to be of great importance as a tool in materials design. Considerable effort is therefore being directed to the provision of more physically based and hence more reliable thermodynamic modelling of the different phases concerned. In this work a method illustrating the modelling of the non-stoichiometric T and Laves phases in the Al-Cu-Mg-Zn system is presented briefly, whereby the minimal information available is used to provide only a small number of parameters for formulation of the Gibbs energy of the phases.
Résumé
Les bases de données thermodynamiques pour les systèmes polyconstitués ont démontré leur importance pour le design des matériaux. Beaucoup d'attention est donné maintenant à une modélisation thermodynamique plus physique pour une description plus valable des systèmes polyphasés.
Une méthode pour la modélisation des phases non-stoechiométriques T et Laves dans le système Al-Cu-Mg-Zn est l'objet du présent travail.
Key words: alloys thermodynamics calphad equilibrium sublattices solubility aluminium copper magnesium zinc
Mots clés : alliages thermodynamique calphad équilibre sous-reseaux solubilité aluminium cuivre magnésium zinc