X-ray investigation of dispersively hardened directionally crystallysed Ni-based alloys

National Technical University of Ukraine, Kiev Polytechnical Institute, Pr Pobedy 37, Kiev 252056, Ukraine.

Abstract

Phase transformation during the process of directional crystallization and following cooling in Ni- based alloys was studied by means of new X-ray method of analysis. It is based on experimental analysis and computer modelling of X- ray diffuse scattering by such alloys. During the production of such single crystals after their cooling the part decompozition of the supersaturated solid solution takes place with the alloyed γ'-phase on the basis of Ni₃Al particles formation, which form Guinie-Preston zones of different size. During the following aging the further excretion of such particles takes place with the changing of their size and quantity. This influences the strength properties of such materials.

Résumé

On a étudié les transformations de phase par metode d’analyse par rayons X an cours de la cristallisation orientee et du refroidissement ulferieur des alliages a base de Ni. La methode est basee sur l’analyse experimentale et la simulation assistée par ordinateur de la dispersion diffuse des rayons X par de tels alliages. Pendant l’obtention des monocristaux de ce type, il se produit, an cours de leur refroidissement, la decomposition partielle de la solution solide sursaturee avec la formation des particules alliees de la γ‘-phase a base des particules Ni₃Al. Elles forment les zones Guinie-Preston de différentes dimensions. Au cours du vieillissement, il se produit le dégagement ulterieur de telles particules avec le changement de leurs dimensions et de leur quantité, ce qui influe sur la solidité de ces matériaux.