Thermodynamic assessment of the Al-Nb system

¹ Laboratoire de métallurgie structurale, URA CNRS 1107, université de Paris-Sud, 91405 Orsay cedex, France.
² Laboratoire de thermodynamique et de physico-chimie métallurgiques, CNRS/INPG/UJF, BP 66, 38402 Saint-Martin-d’Hères cedex, France.

Abstract

The Gibbs energies of formation of the solution and compound phases in the Al-Nb system were derived from an optimisation procedure using all the available experimental thermodynamic and phase diagram data. The non-stoichiometric compounds were modelled with two or three sub-lattices, while a Redlich-Kister polynomial was used to describe the thermodynamic behaviour of the substitutional solutions. A consistent set of thermodynamic parameters with the phase diagram data is obtained.

Résumé

Les enthalpies libres de formation des solutions et des phases non- stoechiométriques existant dans le système Al-Nb ont été obtenues à partir d’une procédure d’optimisation utilisant toutes les informations expérimentales de grandeurs thermodynamiques ou de diagrammes de phases. Le modèle en deux ou trois sous-réseaux a été utilisé pour décrire le comportement thermodynamique des composés non-stoechiométriques alors qu’un polynôme du type Redlich-Kister a été utilisé pour décrire celui des solutions de substitution. Un ensemble cohérent des paramètres thermodynamiques des phases avec le diagramme d’équilibre de phases a été obtenu.